Description and Applications |
HJ600B is a low
hydrogen type electrode for surfacing worn parts of
earth moving equipment, mining machinery, conveyor feed
screws and agricultural implements to be used without
machinery. Metal deposits’ hardness is about 580～610Hv.
Martensitic matrix microstructure provides excellent
wear resistance.
Suitable for the hard facing of mild and alloy steel
components. |
|
|
|
Guideline in Usage |
|
1. |
Electrode should be re-dried
at 300～360℃
for 60 minutes before use. |
|
2. |
Remove dirt such
as oil and dust before welding. |
|
|
|
|
|
|
Typical
Chemical Composition of Weld Metal（％） |
|
C |
Si |
Mn |
P |
S |
Cr |
Mo |
|
0.751 |
0.800 |
1.23 |
0.023 |
0.011 |
4.20 |
0.101 |
|
|
|
|
Typical Hardness of
Weld Metal (Vickers Hardness) |
|
As-Welded |
Tempered at 600℃ |
|
600 |
430 |
|
|
|
|
Size & Recommended Current Range（AC
） |
|
|
|
3.2 |
4.0 |
5.0 |
|
|
350 |
400 |
450 |
|
Current (Amp) |
F |
100~140 |
140~190 |
180~230 |
|
|
|
|
 |