Description and Applications |
HE8018-B1
is a iron powder low hydrogen type electrodes
for welding 0.50% Cr-0.50% Mo steels to be used
at high temperature around 500℃. It is suitable
for welding of high-pressure boiler, chemical
and refinery industries. It has high deposition
rate, with excellent X-ray performance and
mechanical properties, too. |
|
Guideline in Usage |
1. |
Electrode should be re-dried
at 350
~
400℃ for 60 minutes. |
2. |
Preheated
and interpass temperature should be controlled
at 100 ~ 200℃ during welding. Stress relieved
heat treatment at 605~635℃ for one hour. |
3. |
Keep the arc as short as possible. |
|
|
|
Typical
Chemical Composition of Weld Metal(%) |
C |
Si |
Mn |
P |
S |
Mo |
Cr |
0.08 |
0.35 |
0.86 |
0.019 |
0.008 |
0.47 |
0.49 |
|
|
Typical Mechanical Properties of Weld Metal |
Yield Strength
N/mm2 |
Tensile Strength
N/mm2 |
Elongation
% |
Post heat Treatment |
514 |
617 |
25 |
620℃ × 1 hr. |
|
|
Size & Recommended Current Range(AC
) |
|
2.6 |
3.2 |
4.0 |
4.8 |
5.0 |
6.0 |
|
300 |
350 |
350 400 |
350 |
450 |
450 |
Current (Amp) |
F |
60~90 |
90~140 |
150~200 |
190~230 |
190~240 |
240~300 |
V,OH |
50~80 |
80~120 |
120~150 |
140~180 |
140~190 |
- |
|
|
|