Description and Applications |
|
HE308H is the same as
HE308 electrode except that the allowable carbon content
higher than HE308L. It is a lime-Titania type electrode
with 19%Cr- 9%Ni deposited metal. Slag is easy to remove
and arc is stable, spatters are less and bead appearance
is beautiful.
HE308H is suitable for
welding of SUS308H base metal. |
|
|
|
Guideline in Usage
|
|
1. |
Electrodes should be re-dried at
250
∼
300℃ for one hour before use |
|
2. |
Excessively wide weaving may cause welding
defects. Keep weaving width to less than 2.5
times electrode diameter. |
|
|
|
|
|
|
Typical
Chemical Composition of Weld Metal（％） |
|
C |
Si |
Mn |
Ni |
Cr |
Mo |
|
0.06 |
0.720 |
0.760 |
9.85 |
19.13 |
0.030 |
|
|
|
|
Typical Mechanical Properties of Weld Metal |
Yield Strength
N/mm2 |
Elongation
％ |
|
630 |
43 |
|
|
|
|
Size & Recommended Current Range（AC
） |
|
|
|
2.0 |
2.6 |
3.2 |
4.0 |
5.0 |
|
|
250 |
300 |
350 |
350/400 |
450 |
|
Current (Amp) |
F |
30~50 |
60~85 |
85~120 |
115~150 |
150~190 |
|
V,OH |
30~50 |
50~70 |
75~105 |
95~130 |
|
|
|
|
|
 |